High performance, modified polycarboxylate based, set retardant, new generation hyper plasticizer concrete admixture
High performance hyper plasticizing concrete admixture
• In all high-quality concretes where it is desired to have high strength and low water/cement ratio,
• In production of pre-stressed concrete,
• In mass production of concrete by casting,
• Construction elements in different geometries which require complex and detailed molds,
• In production of worksite concretes, precast and prefabricated concretes where fast molding is required,
• In concretes where high early strength is required due to cold climatic conditions,
• In production of self-compacting concrete (SCC).
• Significantly improves the early high strength.
• Reduces molding time in concretes which need high water reduction (25 to 35%) ignificantly reduces the mixing water of concrete.
• Prevent concrete from losing viscosity fast.
• Provides long-term viscosity protection.
• Ensures self-compacting of concrete.
• Allows for achieving high unit weight and strength.
• Ensures achieving less porous and less pervious concretes with a good surface appearance.
• Saves on energy by reducing the curing time and temperature in production of precast members.
• Eliminates the risk of segregation.
• Reduces carbonation rate of concrete, improves its mechanical properties such as shrinkage and creep.
• Increases resistance of concrete to freezing.
• Ensures pumping of the concrete to long distances.
• Does not cause noise pollution since it does not require vibration.
• Dosage of contribution is based on the aggregate properties, water quality, concrete class, water-cement ratio and temperature of place. Therefore, it is recommended to determine the dose by preparing test mixtures in a laboratory.
• When adjusting the consistency, high water cut-off property of admixture should be taken into account and more water addition should not be done to mixture.
| Kimyasal İçeriği / Chemical Contents | : | Polikarboksilat esaslı / Polycarboxylate based | |
| Görünüm-Renk / Appearance-Colour | : | Kahverengi sıvı / Brown liquid | |
| Yoğunluk / Density | : | 1.06 ± 0.02 kg/l. | ISO 758 |
| pH Değeri / pH Value | : | 5.0 ± 1 | TS 6365 EN 1262 |
| Klor İçeriği / Chloride Content (Cl) | : | < % 0.1 | TS EN 480-10 |
| Alkali İçeriği / Alkali Content | : | < % 4 | TS EN 480-12 |
| Donma Noktası / Freezing Point | : | -4 ºC | |
| Korozyon Davranışı / Corrosion Behavior | : | Sadece TS EN 934-1 Ek A.1’de verilen bileşenleri içerir. Contains only components according to TS EN 934-1 Annex A.1 |
|
| Tehlikeli Maddeler / Dangerous Substances | : | Tamamen Ek ZA’ye uygundur. / Comply with annex ZA. | |
| +20ºC’de, %50 bağıl nem koşullarında elde edilmiştir. / Is produced at +20ºC, %50 relative humidity conditions. | |||